二氧化硅衬底的全区域覆盖的单层二硫化钼

简要描述:This product contains full area coverage MoS2 monolayers on SiO2/Si substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick MoS2 sheet.

  • 更新时间:2022-07-15
  • 产品型号:
  • 厂商性质:生产厂家
  • 访  问  量:216

详细介绍

This product contains full area coverage MoS2 monolayers on SiO2/Si substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick MoS2 sheet. Synthesized full area coverage monolayer MoS2 is highly luminescent and Raman spectroscopy studies also confirm the monolayer thickness. In comparison to full area coverage MoS2 on sapphire, full area coverage MoS2 on SiO2/Si display higher PL intensity.



Sample Properties.

Sample size

1cm x 1cm square shaped

Substrate type

Thermal oxide (SiO2/Si) substrates

Coverage

Full Coverage Monolayer

Electrical properties

1.85 eV Direct Bandgap Semiconductor

Crystal structure

Hexagonal Phase

Unit cell parameters

a = b = 0.313 nm, c = 1.230 nm,

α = β = 90°, γ = 120°

Production method

Atmospheric Pressure Chemical Vapor Deposition (APCVD)

Characterization methods

Raman, photoluminescence, TEM, EDS

Specifications

1)    Identification. Full coverage 100% monolayer MoS2 uniformly covered across SiO2/Si substrates.

2)    Physical dimensions. One centimeter in size. Larger sizes up to 2-inch wafer-scale available upon requests.

3)    Smoothness. Atomically smooth surface with roughness < 0.2 nm.

4)    Uniformity. Highly uniform surface morphology. MoS2 monolayers uniformly cover across the SiO2/Si substrates.

5)    Purity. 99.9995% purity as determined by nano-SIMS measurements

6)    Reliability. Repeatable Raman and photoluminescence response

7)    Crystallinity. High crystalline quality, Raman response, and photoluminescence emission comparable to single crystalline monolayer flakes.

8)    Substrate. SiO2/Si substrates. But our research and development team can transfer MoS2 monolayers onto variety of substrates including PET and quartz without significant compromisation of material quality.

9)    Defect profile. MoS2 monolayers do not contain intentional dopants or defects. However, our technical staff can produce defected MoS2 using α-bombardment technique.


Supporting datasets [for 100% Full area coverage on SiO2/Si]



Transmission electron images (TEM) acquired from CVD grown full area coverage MoS2 monolayers on SiO2/Si confirming highly crystalline nature of monolayers


Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage MoS2 on SiO2/Si confirming Mo:S 1:2 ratios


Room temperature photoluminescence spectroscopy (PL) and Raman spectroscopy (Raman) measurements performed on CVD grown full area coverage MoS2 monolayers on SiO2/Si. Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples and PL spectrum display sharp and bright PL peak located at 1.85 eV in agreement with the literature.


产品咨询

留言框

  • 产品:

  • 您的单位:

  • 您的姓名:

  • 联系电话:

  • 常用邮箱:

  • 省份:

  • 详细地址:

  • 补充说明:

  • 验证码:

    请输入计算结果(填写阿拉伯数字),如:三加四=7
泰州巨纳新能源有限公司
  • 联系人:陈谷一
  • 地址:江苏省泰州市凤凰西路168号
  • 邮箱:taizhou@sunano.com.cn
  • 电话:021-56830191
联系我们

扫一扫以下二维码了解更多信息

销售微信咨询

网站二维码

版权所有©2023泰州巨纳新能源有限公司All Rights Reserved    备案号:苏ICP备17000059号-2    sitemap.xml    总访问量:18739
管理登陆    技术支持:化工仪器网